B?HLER FOX CN 18/11不銹鋼焊條

Description
Basic coated, core wire alloyed electrode with controlled delta ferrite content (3-8 FN) for aus-
tenitic CrNi steels with increased carbon contents (e.g. 1.4948 / 304H), in the boiler, reactor and
turbine fabrication. Approved in long-term condition up to +700 °C service temperature (300 °C
in the case of wet corrosion). Resistant to hot cracking, scaling and corrosion. Excellent
weldability in all positions except vertical down. Also suitable for German material no. 1.4551
and no. 1.4550, which are approved for temperatures up to +550 °C.
Approvals and Certificates
TüV-D (0138.), KTA 1408 1 (8067.00), TüV-A (447), CL (0332), UDT, LTSS, SEPROZ
Same Alloy/Similar Alloy Filler metals
SMAW stick electrode: FOX E 308 H GMAW flux cored wire: E 308 H-FD
GTAW rod: ER 308 H-IG E 308 H PW-FD
CN 18/11-IG SAW combination: CN 18/11-UP/BB 202
GMAW solid wire: CN 18/11-IG
base Materials
similar alloyed creep resistant steels
1.4948 X6CrNi18-11, 1.4949 X3CrNiN18-11
AISI 304H, 321H, 347H
Operating Data
re-drying if necessary: ? mm L mm amps A
250 - 300 °C, min. 2 h 2.5 250 50 - 180
electrode identification:  3.2 350 80 - 100
FOX CN 18/11 308-15 E 19 9 B 4.0 350 110 - 140
Preheating is not required, only in case of wall thickness above 25 mm preheat up to 150 °C
Interpass temperature should not exceed 200 °C.
Mechanical Properties of All-weld metal
(*) u
yield strength R e N/mm 2 : 420 (≥ 350)
tensile strength R m N/mm 2 : 580 (≥ 550)
elongation A (L 0 = 5d 0 ) %: 40 (≥ 335)
impact work ISO-V KV J + 20 °C: 85 (≥ 370)
(*)  u untreated, as-welded
Typical Composition of All-weld metal
C Si Mn Cr Ni FN
wt-% 0.05 0.3 1.3 19.0 10.3 3-8