| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 阻燃性 | --- | UL 94 | V-0 | --- |
| 阻燃性 | --- | UL 94 | 0.8 | mm | |
| 比重 | --- | ASTM D-792 | 1.15 | --- | |
| 模具收縮率 | 1.6mm | --- | 0.8 | --- | |
| 模具收縮率 | 3.2mm | --- | 1.1 | --- | |
| 機(jī)械性能 | 拉伸強(qiáng)度 | --- | ASTM D-638 | 89.6 | MPa |
| 斷裂伸長(zhǎng)率 | --- | ASTM D-638 | 14 | % | |
| 彎曲模量 | --- | ASTM D-790 | 3450 | MPa | |
| IZOD沖擊強(qiáng)度 | --- | ASTM D-256 | 43 | J/m | |
| 熱 性 能 | 熔點(diǎn) | --- | ASTM D-3418 | 264 | ℃ |
| 熱變形溫度 | 0.45MPa | ASMT D-648 | 230 | ℃ | |
| 熱變形溫度 | 1.80MPa | ASTM D-648 | 70 | ℃ | |